Titanium

Cp-Ti Grade 2

Pure Titanium powders, commonly know as Cp-Ti, are used extensively in the medical field for a wide range of applications, due to the biocompatibility of Titanium with the human body. As an ISO 13485 accredited  supplier, AP&C commits  to  meeting  the  highest  quality  standards  for  medical  applications, while offering premium-quality powders, that are high in purity and batch-to-batch consistency. AP&C’s APATM plasma-atomized Cp-Ti powders also feature high-sphericity, low levels of entrapped and surface porosities, and minimal satellite content.

 

High purity titanium: Cp-Ti grade 2

Powder chemistry may comply with standards: ASTM B348, ASTM F67, ASTM F1580
Typical particle size distributions (PSD): 0-20 μm, 15-45 μm, 15-63 μm, 45-106 μm, 45-150 μm
 

 SD  Size distribution by laser diffraction (ASTM B822)  Apparent density (ASTM B212)  Flow rate (ASTM B213)  Oxygen content
 D10  D50  D90
 0-25 µm  6 µm   12 µm  21 µm  2.7 g/cm3*   -  0.19 %
 15-45 µm  17 µm  32 µm  44 µm  2.55 g/cm3  29 s  0.19 %
 15-63 µm  19 µm  36 µm  50 µm  2.56 g/cm3  27 s  0.19 %
 45-106 µm  50 µm  74 µm  100 µm  2.61 g/cm3  23 s  0.19 %
 45-150 µm  55 µm  82 µm  120 µm  2.62 g/cm3  25 s  0.19 %

*Tap density per ASTM B527



 

Cp-Ti2

Particle size distribution is measured by laser diffraction as per ASTM B822.  Due to the high sphericity and very low satellites present on AP&C powder, the particle size distribution is highly uniform and the D10, D50 and D90 meet and exceed the industry requirements with an exceptional batch to batch reliability. The typical powder atomization yield ranges from 0-150 µm, after atomization, the powder is sieved according customer specifications.