Cp-Ti Grade 1
Pure Titanium powders, commonly know as Cp-Ti, are used extensively in the medical field for a wide range of applications, due to the biocompatibility of Titanium with the human body. As an ISO 13485 accredited supplier, AP&C commits to meeting the highest quality standards for medical applications, while offering premium-quality powders, that are high in purity and batch-to-batch consistency. AP&C’s APATM plasma-atomized Cp-Ti powders also feature high-sphericity, low levels of entrapped and surface porosities, and minimal satellite content.
High purity titanium: Cp-Ti grade 1
Powder chemistry may comply with standards: ASTM B348, ASTM F67, ASTM F1580
Typical particle size distributions (PSD): 0-20 μm, 15-45 μm, 15-63 μm, 45-106 μm, 45-150 μm
|SD||Size distribution by laser diffraction (ASTM B822)||Apparent density (ASTM B212)||Flow rate (ASTM B213)||Oxygen content|
|0-25 µm||6 µm||12 µm||21 µm||2.7 g/cm3*||-||-|
|15-45 µm||17 µm||32 µm||44 µm||2.55 g/cm3||29 s||0.13 %|
|15-63 µm||19 µm||36 µm||50 µm||2.56 g/cm3||27 s||0.11 %|
|45-106 µm||50 µm||74 µm||100 µm||2.61 g/cm3||23 s||0.10 %|
|45-150 µm||55 µm||82 µm||120 µm||2.62 g/cm3||25 s||0.10 %|
*Tap density per ASTM B527
Particle Size Distribution
Cp-Ti Grade 1
Particle size distribution is measured by laser diffraction as per ASTM B822. Due to the high sphericity and very low satellites present on AP&C powder, the particle size distribution is highly uniform and the D10, D50 and D90 meet and exceed the industry requirements with an exceptional batch to batch reliability. The typical powder atomization yield ranges from 0-150 µm, after atomization, the powder is sieved according customer specifications.